6082 aluminium alloy is an alloy in the wrought aluminium-magnesium-silicon family (6000 or 6xxx series). It is one of the more popular alloys in its series (alongside alloys 6005, 6061, and 6063), although it is not strongly featured in ASTM (North American) standards. It is typically formed by extrusion and rolling, but as a wrought alloy it is not used in casting. It can also be forged and clad, but that is not common practice with this alloy. It cannot be work hardened, but is commonly heat treated to produce tempers with a higher strength but lower ductility.[1]

Alternate names and designations include AlSi1MgMn, 3.2315, H30, and A96082. The alloy and its various tempers are covered by the following standards:[2]

  • EN 485-2: Aluminium and aluminium alloys. Sheet, strip and plate. Mechanical properties
  • EN 573-3: Aluminium and aluminium alloys. Chemical composition and form of wrought products. Chemical composition and form of products
  • EN 754-2: Aluminium and aluminium alloys. Cold drawn rod/bar and tube. Mechanical properties
  • EN 755-2: Aluminium and aluminium alloys. Extruded rod/bar, tube and profiles. Mechanical properties
  • ISO 6361: Wrought Aluminium and Aluminium Alloy Sheets, Strips and Plates

Chemical composition

The alloy composition of 6082 aluminium is:[2]

Aluminium 6082 Chemical Composition
Element Weight Percentage (%)
Aluminium 95.2 to 98.3
Chromium 0.25 % max.
Copper 0.1 % max.
Iron 0.5 % max
Magnesium 0.6 to 1.2%
Manganese 0.4 to 1.0 %
Silicon 0.7 to 1.3%
Titanium 0.1 % max
Zinc 0.2 % max
residuals 0.15 % max

Properties

Typical material properties for 6082 aluminum alloy include:[2]

Properties of 6082 Aluminium
Properties Value
Density 2.71 gm/cc
Young's modulus 71 GPa
Ultimate tensile strength 140 to 330 MPa
Yield strength 260 MPa
Thermal Expansion 23.1 μm/m-K.

References

  1. ↑ Marks' Standard Handbook for Mechanical Engineers, 8th Ed., McGraw Hill, pp. 6-50 to 6-58
  2. 1 2 3 6082 (AlSi1MgMn, 3.2315, H30, A96082) Aluminum. Retrieved on 2014-12-31.

Aluminum alloy table

This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.