Lutetium aluminum garnet (commonly abbreviated LuAG, molecular formula Lu3Al5O12) is an inorganic compound with a unique crystal structure primarily known for its use in high-efficiency laser devices. LuAG is also useful in the synthesis of transparent ceramics.[1]

LuAG is a dopable scintillating crystal that will demonstrate luminescence after excitation. Scintillating crystals are selected for high structural perfection, high density and high effective atomic number. LuAG is particularly favored over other crystals for its high density and thermal conductivity. LuAG has a relatively small lattice constant in comparison to the other rare-earth garnets, which results in a higher density producing a crystal field with narrower linewidths and greater energy level splitting in absorption and emission.[2] These properties make it an excellent host for active ions such as Yb, Tm, Er, and Ho employed in diode-pumped solid-state lasers.

The density of the lutetium crystal is greater than that of other metals, such as yttrium, meaning that the crystal properties do not change with the addition of dopant ions.[3] It can be especially useful for high energy particle detection and quantification on account of its density and thermal stability. This high melting temperature, in addition to the lack of availability of lutetium has made this crystal less commonly used than its fellow garnets, despite its favorable physical properties.[1]

Physical properties and structure

Lutetium aluminum garnet, with the molecular formula Lu3Al5O12, has a complex cubic crystal structure. The unit cell contains 24 lutetium atoms in c sites, 96 oxygen atoms in h sites, and aluminum in 16 a sites and 24 d sites.[4]

The mass of the lutetium ion is closer to laser-active lanthanides which are used for doping, meaning that the thermal conductivity is not altered as it would be in other garnet structures at higher doping levels. Additionally, the crystal radius of lutetium limits the alterations observed in the crystal structure with doping present.[1]

Physical properties of LuAG[2]
Chemical formula Lu3Al5O12
Crystal structure Cubic
Molecular weight 851.81 g/mol
Density 6.71 g/cm3
Melting Point 1980 ˚C
Specific Heat 0.419 J/gK

Synthesis

Lutetium aluminum garnet is an artificial crystal that can be grown using a technique developed approximately a century ago, the Czochralski growth process. This method allows for the formation of single-crystal cylinders of various scintillators. The method is utilized for the growth of semiconductors, oxides, fluorides, and halide crystals in addition to metal crystals.[5]

LuAG's growth process is relatively simple due to its crystallographic structure and physiochemical properties. Because of the materials' thermal stability, it requires an apparatus to manage a high power supply and temperatures of up to 2500 ˚C.[5]

Hydrothermal growth of garnets has been recorded since the 1960s and has now been demonstrated for LuAG as an alternative technique to the traditional melt method employed in the past. This method enables crystals to be grown at lower temperatures, limiting the thermally induced defects which result in expanses of optically useless crystal.[1]

This method was employed without the use of LuAG seed on account of its unavailability and cost. Instead, the growth was performed using yttrium aluminium garnet crystals with a minimal lattice mismatch of 0.6%. The growth was done using powdered lutetium(III) oxide and crushed sapphire feedstock with 2M potassium bicarbonate mineralizer with a thermal gradient of 610 - 640 ˚C.[1]

Applications

The lasing process involving aluminum garnet crystals is carried out by the dopant atoms, usually rare-earth metals, which take the place of a few atoms of the original metal in the crystal structure (in this case lutetium). The role of the unsubstituted atoms of lutetium, aluminum, and oxygen function as support for the dopant ions.

See also

References

  1. 1 2 3 4 5 Moore, Cheryl (2015). "Towards a Greater Understanding of Hydrothermally Grown Garnets and Sesquioxide Crystals for Laser Applications". Clemson University Tiger Prints. Bibcode:2015PhDT.......308M.
  2. 1 2 "Lutetium Aluminum Garnet - LuAG - Lu3Al5O12". scientificmaterials.com. Retrieved 2016-04-29.
  3. Kiss, Z. J.; Pressley, R. J. (1966-10-01). "Crystalline Solid Lasers". Applied Optics. 5 (10): 1474–86. Bibcode:1966ApOpt...5.1474K. doi:10.1364/ao.5.001474. ISSN 1539-4522. PMID 20057583.
  4. Kuwano, Yasuhiko; Suda, Katsumi; Ishizawa, Nobuo; Yamada, Toyoaki (2004-01-02). "Crystal growth and properties of (Lu,Y)3Al5O12". Journal of Crystal Growth. 260 (1–2): 159–165. Bibcode:2004JCrGr.260..159K. doi:10.1016/j.jcrysgro.2003.08.060.
  5. 1 2 Yoshikawa, A.; Chani, V.; Nikl, M. (2013). "Czochralski Growth and Properties of Scintillating Crystals". Acta Physica Polonica A. 124 (2): 250–264. Bibcode:2013AcPPA.124..250Y. doi:10.12693/aphyspola.124.250.
This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.